    How to soft solder?

    Not a how to, but a request to tell me how to.

    I’ve been trying to soft solder mild steel and having zero luck! I’ve got good clean metal and can get the solder to adhere to one piece but not both. I wondered if it maybe my flux or solder but I can’t for the life of me find a recommendation of what others have used. Plenty saying to use silver solder but I don’t want to heat the steel to 600C, I’d be much happier at 400C as it’s been strong enough for most jobs over the last hundred years.

    Any recommendations?
    Information
    Warning: This is a relatively older thread
    This discussion is older than 360 days. Some information contained in it may no longer be current.

  2. # ADS
    Friends and Sponsors
    Join Date
    October 2006
    Posts
    All Threads
    A Collector's View - The SMLE Short Magazine Lee Enfield 1903-1989. It is 300 8.5x11 inch pages with 1,000+ photo’s, most in color, and each book is serial-numbered.  Covering the SMLE from 1903 to the end of production in India in 1989 it looks at how each model differs and manufacturer differences from a collecting point of view along with the major accessories that could be attached to the rifle. For the record this is not a moneymaker, I hope just to break even, eventually, at $80/book plus shipping.  In the USA shipping is $5.00 for media mail.  I will accept PayPal, Zelle, MO and good old checks (and cash if you want to stop by for a tour!).  CLICK BANNER to send me a PM for International pricing and shipping. Manufacturer of various vintage rifle scopes for the 1903 such as our M73G4 (reproduction of the Weaver 330C) and Malcolm 8X Gen II (Unertl reproduction). Several of our scopes are used in the CMP Vintage Sniper competition on top of 1903 rifles. Brian Dick ... BDL Ltd. - Specializing in British and Commonwealth weapons Specializing in premium ammunition and reloading components. Your source for the finest in High Power Competition Gear. Here at T-bones Shipwrighting we specialise in vintage service rifle: re-barrelling, bedding, repairs, modifications and accurizing. We also provide importation services for firearms, parts and weapons, for both private or commercial businesses.
     

  3. #2
    Contributing Member rcathey's Avatar
    Join Date
    Dec 2012
    Last On
    Yesterday @ 11:56 AM
    Location
    St. Louis, MO Area
    Posts
    1,645
    Local Date
    03-28-2024
    Local Time
    09:13 AM
    I'm by no means an expert but I have done some here and there over the course of my career.
    My first guess is you don't have both pieces of metal hot enough. By the sound of it, one piece is hot enough and that's where the solder is sticking.

    If one piece is considerably thicker than the other, focus your heat source on it first. Once it gets where you need it, start pushing that heat over to the thinner piece.

    Long story short, the solder is going where the heat is and staying there.

  4. Avoid Ads - Become a Contributing Member - Click HERE
  5. #3
    Contributing Member Flying10uk's Avatar
    Join Date
    Feb 2015
    Last On
    Yesterday @ 10:53 PM
    Location
    UK
    Posts
    5,075
    Local Date
    03-28-2024
    Local Time
    02:13 PM
    I can only explain the full process of how I soft solder which works for me. I can't just explain part of the process, sorry.

    For soft solder I would say your problem is not having the metal clean enough to start with and, if I was a gambling man, too much heat. Soft solder will only work correctly when the correct heat range is used, get it too hot and the joint starts turning black. Once the joint has turned black your efforts are wasted and no amount of jiggery-pokery will salvage the joint.

    To start the process throughly clean both pieces of metal that you wish to soft solder so that they are shiny clean and you could use abrasive paper for this. Coat each surface that you wish to solder together and which you have just cleaned with an "active flux" suitable for soft soldering (this type of flux also cleans the metal as it gets hot). You then need to "tin" both surfaces with solder and you basically use just enough heat on the surface of the metal to melt the solder. If you do not first tin the surfaces with mild steel then, in my experience, you will never get them to soft solder together. Do NOT over-heat the metal, do NOT burn the solder and do NOT melt the solder onto the metal. Once both surfaces are covered in solder they both need to be "wiped off" while the solder is still hot leaving a thin even film of solder over each surface. I normally just use a cotton or non nylon piece of rag for this purpose. Hands should be protected with heat resistant gloves while the hot soldered surfaces are wiped down and care taken while this is carried out. All necessary personal protective equipment should be worn.

    Once both surfaces have been properly tinned and "wiped off" apply further soldering flux to each of the surfaces that you have just tinned and if it is a wide joint you may wish to lay some small additional pieces of flattened solder, off the reel, onto the join. Place the 2 pieces of metal together which may also need some form of clamping. Next apply heat but do NOT over-heat and do NOT get the flame too close to the metal. Heat the join evenly, slowly and gently from a distance and once the flux starts to bubble and smoke you know that soon the metal will be up to temperature. Test the temperature of the metal by applying the solder but do NOT heat the solder onto the metal. Keep heating slowly and gently, over the area to be soldered, until the metal melts the solder and then back-off with the flame. Apply enough heat and solder to the joint as required but do NOT over-heat. If you over-do it with the heat and the joint turns black, no amount of additional heat, flux or solder will salvage the joint and it will be back to square one.

    It is good practice to wipe down the soldered joint with a damp cloth when an "active flux" has been used but not everyone does.

    Do please wear your personal protective equipment such things as gloves and googles.
    Last edited by Flying10uk; 12-05-2019 at 08:10 PM.

  6. The Following 3 Members Say Thank You to Flying10uk For This Useful Post:


  7. #4
    Legacy Member Brit plumber's Avatar
    Join Date
    Dec 2009
    Last On
    03-25-2024 @ 02:00 PM
    Posts
    1,807
    Local Date
    03-28-2024
    Local Time
    03:13 PM
    Thread Starter
    Thanks gents, I’ve pretty much done as described except I think Flying10 has identified my issue, to much heat! My steel turns black so I shall try less heat and see if that works. I shall report back.

    Do you guys just use regular solder?

  8. #5
    Contributing Member Flying10uk's Avatar
    Join Date
    Feb 2015
    Last On
    Yesterday @ 10:53 PM
    Location
    UK
    Posts
    5,075
    Local Date
    03-28-2024
    Local Time
    02:13 PM
    I don't "overly worry" about what soft solder I use as fluxed and non fluxed will work. The variations of soft solder available will work at slightly varying temperatures. If you follow the correct soldering procedure most soft solders should work.

    What is important, especially with steel and copper but also with other metals is to "properly clean" the metal first and this means that you do actually have to go over the surface with something like emery paper/cloth and or wire wool first. Just because the metal may look clean when you acquire it does not mean that you do not have to "properly clean" it first. Failure to "properly clean" the surface first will result in a poor join or no join.

    To solder steel together the surfaces must be first "tinned", as already described. Failure to "tin" the surfaces of the steel first will result in complete failure of the attempt to solder the steel together.

    Do not use too much heat and heat slowly and evenly using only just enough heat required to melt the solder. Using too much heat will completely destroy the attempt to solder. You are not attempting to replicate a blast furnace in your shed/workshop, your are soft soldering which melts at a relatively low temperature.

  9. The Following 2 Members Say Thank You to Flying10uk For This Useful Post:


  10. #6
    Contributing Member Flying10uk's Avatar
    Join Date
    Feb 2015
    Last On
    Yesterday @ 10:53 PM
    Location
    UK
    Posts
    5,075
    Local Date
    03-28-2024
    Local Time
    02:13 PM
    This was the best video that I could find to describe the "tinning process". Although the "tinning" in this video is for the purpose of lead loading a car body the process is the same as required for other purposes.

    Notice the importance given to the cleaning of the metal and notice the "wiping off" of the tinned surface while still hot.

    The "tinning compound" mentioned in the video is basically a mixture of flux and powdered solder.


  11. Thank You to Flying10uk For This Useful Post:


  12. #7
    Legacy Member 3006guns's Avatar
    Join Date
    Jun 2018
    Last On
    05-12-2020 @ 11:28 PM
    Location
    Alturas, California
    Posts
    6
    Local Date
    03-28-2024
    Local Time
    07:13 AM

    Johnson's tinning compound..........

    This is my first post on this particular gun website, so be gentle.

    There is a liquid compound that is sold as "Johnson's Tinning Compound". Been around forever and used mostly in auto body work. It's chief claim to fame is that it is absolutely guaranteed to get solder to adhere to steel. I've used it to secure Mauser rear sight bases and it works just fine.

    I might be off on that name as it's been a few years, but any decent auto supply store should be able to locate it. I'd suggest trying it on a few scrap pieces of steel first to get the "hang" of it.

  13. #8
    Contributing Member Flying10uk's Avatar
    Join Date
    Feb 2015
    Last On
    Yesterday @ 10:53 PM
    Location
    UK
    Posts
    5,075
    Local Date
    03-28-2024
    Local Time
    02:13 PM
    "Tinning compounds" are normally a flux of some description with a certain amount of powdered solder already added to the flux.

  14. #9
    Advisory Panel Chuckindenver's Avatar
    Join Date
    Mar 2009
    Last On
    Yesterday @ 12:08 PM
    Location
    Denver Co
    Age
    61
    Posts
    3,150
    Real Name
    chuck
    Local Date
    03-28-2024
    Local Time
    08:13 AM
    heat the work, not the solder.... patience is key. clean stainless wire brush to clean the surface.. good quality flux
    warpath metal finishing contact info.
    molinenorski@msn.com
    720-841-1399 during normal bus, hours.

  15. The Following 2 Members Say Thank You to Chuckindenver For This Useful Post:


  16. #10
    Legacy Member bombdoc's Avatar
    Join Date
    Aug 2012
    Last On
    03-14-2024 @ 05:12 PM
    Location
    UK
    Posts
    170
    Local Date
    03-28-2024
    Local Time
    02:13 PM
    A very old fashioned flux for soft soldering is zinc chloride. This is made by dropping bits of zinc into Hydrochloric acid until it stops reacting.. hence the old name of "killed spirits" (..from "Spirits of Salt" the old name for Hydrochloric Acid)..

    It is neither gentle or pleasant, but it will usually work were others don't.. it does however corrode like hell afterwards, so the joint will need a good clean with hot water and elbow grease!

+ Reply to Thread
Page 1 of 2 1 2 LastLast

Similar Threads

  1. Removal of silver solder?
    By Kiwi in forum Gunsmithing for Old Milsurps
    Replies: 9
    Last Post: 04-23-2015, 08:43 PM
  2. L42A1 Soft Case
    By chosenman in forum The Lee Enfield Knowledge Library Collectors Forum
    Replies: 19
    Last Post: 02-05-2014, 06:20 PM
  3. soft soldering pads no4 mk1 T
    By savage in forum The Lee Enfield Knowledge Library Collectors Forum
    Replies: 4
    Last Post: 03-18-2012, 01:06 AM
  4. IVI soft point loads
    By big bear in forum Ammunition and Reloading for Old Milsurps
    Replies: 8
    Last Post: 07-27-2010, 01:47 PM
  5. Parkerizing and solder
    By edon in forum The Restorer's Corner
    Replies: 3
    Last Post: 03-06-2009, 10:18 PM

Tags for this Thread

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
Raven Rocks