Legacy Member
Have you ever seen Rolls Royce remove a dent? These guys are amazing! They heat the dent up and then use the (I want to say hammer) dollies to remove the dent and then they super heat it and do something else and when the metal cools, it shrinks and thickens the metal up again, how the hell does that work!
-
-
09-09-2014 03:46 PM
# ADS
Friends and Sponsors
-
You can't defeat the laws of physics BP! I doubt whether that can thicken the material but you can loose any stretch 'a bit' by using a panel file somehow or another. When I was teaching I used to show an example of bending = lengthening = reducing thickness. But a badly dented Sten or Sterling tube was scrapped. We used to certify destruction and send the guillotined-off serially numbered mag housing back tied to the 1043-A paperwork
-
-
-
Legacy Member
I think the Mk4 casings might have been made from different steel than the Patchett casings. When welding the Patchett I noticed the steel seemed less prone to Martensite, glass like crystals. Too much Martensite will make the steel too hard, brittle and prone to “cold cracking.” It was cold cracking that sent some Liberty Ships to the bottom. Not enough Martensite will leave the steel soft.
It turns out the Mk4 casing steel contains a high level of manganese. That means it’s probably a Reynolds steel. Though it’s not the one I thought it might be. It’s definitely not the Accles and Pollock chromium-molybdenum.
My guess is Sterling changed to the high CE manganese steel when they stopped welding components to the casing and started using only induction brazing. The few small spot welds are insignificant. The manganese steel is perfect for brazing but poor for welding due to the high CE, equivalent carbon content.
Those Sterling engineers really knew their onions. They used the right steel for their manufacturing process. They must also have known how strong and durable it would be.
Using manganese has been around for a long time. The Spartans swords were made from iron ore containing manganese. It made them stronger than their enemy’s swords and gave them an edge in battle. But it wasn’t widely used until around WWI. That’s when items made from “Hadfield steel” or “Mangalloy” began to be mass produced. It has a very high manganese content. It’s also non-magnetic. The Type B Brodie helmet was made from it.
Last edited by Vincent; 09-15-2014 at 01:12 PM.
-
Thank You to Vincent For This Useful Post:
-
Legacy Member
Now I know what steel it is I can heat treat and temper it correctly. Should be able to do it over the weekend.
I made the front sight protector. It's like the lower left one of the four together on page 91. Now if I could only find it!
-