Hello all, can anyone please tell me what steel is used to cast L3A1 Bayonets?
Many Thanks, Chris
Hello all, can anyone please tell me what steel is used to cast L3A1 Bayonets?
Many Thanks, Chris
Are they not drop forged? A drop forging can have the appearance of a casting because of how it's forged, i.e. an upper and lower former to forge the steel.
They were Investment cast made on a tree of about 6 or 8 at a time.
They were made at the Vickers Factory called Trucast, in Ryde, on the Isle of Wight.
The factory also made the Spirit of Ecstasy bonnet mascots used on Rolls Royce vehicles and Turbo Hot End wheels. amongst other things.
The factory is now closed and built on for housing.
The bayonets were first made in green wax, joined to the trees, ceramic coated, the wax melted out, then the metal melted into the mould in a vacuum chamber.
I used to work there.
I can't tell you what the metal was though, I am afraid, just long round bars of steel.
it probably was stainless. Most everything that we cast was stainless of some grade
Steel, or aluminum? Seems like I saw one made from aluminum at the SOS a few years ago.
The actual steel was always a problem because this particular bayonet had many demands placed on it. It was a knife and therefore had to bend. But in bending, the tips were always snapping off. It was also a cutter so the shearing side had to retain its edge. It had to be all things to all men and for many years there wasn't one steel that could do all things. Throw stainless into the mix adds a new dimension. At one time certain regiments wanted them to be suitable for chroming - that was a non runner after several attempts. But Nickel plating worked.
All this......., as cheaply as possible. Mind you, whatever sort you came across, they were extremely tough material and drilling/tapping them for presentation pieces was a xxxxxxx nightmare
That aside, everyone wanted their finger in the bayonet pie. Bottle openers, tin openers, letter openers, daggers, duck-board chopper uppers, hot and cold running water......... One report I read, from a plain speaker who has just passed away suggested just leave it as a means of stabbing people. It would be as cheap to and give everyone a Leatherman to do everything else
Does anyone remember the early ones with serial numbers engraved in the groove. Very hard but the breaking tips made them useless!
That's what they finally did with us. That eliminated the useless clasp knives.Originally Posted by Peter Laidler
Regards, Jim