Thanks erik3D, thats interesting. Next time I have it out, I'll try to scratch those areas and see if they remained hard. I'm guessing C scale, HRC 53 is not that hard. They may be far enough from the cutting and welding to have survived. The welded receiver was easily machined, no hardening. So originally maybe a case hard or surface hardening?