I would be interested to know the name of this finishing process from this company, would it be normal hot blacking or a pre dip phosphate process.
Quote Originally Posted by Peter Laidlericon View Post
You've totally lost me tankie........

There are small steel finishers that dip steel components in an acid bath that only affects any surface material. It is neutralised and then bathed in a chemical that puts a deep black chemically induced finish onto the steel. Wouldn't stand too much rolling around in the back of your old Bedford or FV-432 but does look very good. Saw a No32 and 42 done like it and it looked good..........