It would be an interesting exercise to run some samples through an x-ray spectrometer and see exactly what was used.

I have noticed different stripped receivers have a different ring, but is it the steel or the heat treatment?

In case of the Patt.14 rifles at Eddystone for example it seems to have been the forging/heat treatment than the steel itself.