Any of you guys know about metallurgy, have an opinion or experience with this.
I have this MLE barrel action that was deactivated by brazing the bolt in place with brass.
Now even to me it is quite clear that the receiver and bolt are toast.
But i am wondering if the barrel might be salvageable ?
Would the heat from brazing the receiver have affected it ?
No holes were made anywhere, no rod welded and no DP markings.
I'm asking because i have this 1893 MLM Mk II action that i would like to mate with a barrel and rescue it.